Property | Value |
Packaging | Part A: 4 kg, Part B: 4.7 kg, Part C: 20 kg |
Mix Ratio (by volume) | A:B:C – Mix full units only |
Gel Time (@ 25°C) | 15–20 minutes |
VOC Content | <10 g/L |
Shelf Life | 12 months (unopened, cool/dry place) |
Full Cure Time | 5 days |
Coverage | ¼″ (6 mm): 30 ft² / 29.4 kg ⅛″ (3 mm): 60 ft² / 29.4 kg |
Property | Value |
Tensile Strength | 1045 psi |
Concrete Adhesion | 300 psi |
Flexural Strength | 16.2 MPa (2350 psi) |
Hardness (Shore D) | 82–87 |
Taber Abrasion | 0.12 g loss (CS17, 1000g, 1000 cycles) |
Water Absorption | 0.12% |
Thermal Expansion Coefficient | 1.6 × 10⁻⁵ mm/mm/°C (0.89 × 10⁻⁵ in/in/°F) |
Softening Point | 130°C (266°F) |
Specific Gravity | Part A: 1.0 Part B: 1.24 |
Viscosity | 82–87 (unit not specified) |