IC-100 MVB is a 100% solids, two-component moisture vapor barrier epoxy coating designed for use on concrete under various floor coverings (e.g., vinyl tiles, hardwood). It serves as a primer, bonding agent, or topcoat with a long pot life and fast-curing capabilities at ambient and low temperatures. Controls moisture vapor emission up to 25 lb/24 hr/1000 ft².
- Dense surface: bacteria/moisture resistant, easy to clean
- Excellent self-adhesion for multiple layers
- Strong adhesion to various substrates
Parameter | Value |
Packaging | 11.35 L (3 US gal), 56.7 L (15 US gal) |
Color | Part A: Upon Request; Part B: Clear to Amber |
Mix Color | Upon Request |
Mix Ratio (by volume) | A:B = 2:1 (100:50) |
Mix Ratio (by weight) | A:B = 100:39:45 |
Gel Time (100g @ 25°C) | 35–40 minutes |
Pot Life (100g @ 25°C) | 20 minutes |
Solids Content | 100% (weight & volume) |
VOC | 25 g/L |
Viscosity @ 25°C | Clear: A: 1200–1400, B: 2000–2300, Mix: 1800–2200 cP Colors: A: 1500–1900, B: 2000–2300, Mix: 2300–2500 cP |
Specific Gravity | Clear: A: 1.14, B: 0.9–1.0 Colors: A: 1.15–1.20, B: 0.9–1.0 |
Thinner Recommended | Xylene |
Shelf Life | 12 months (sealed, away from moisture/extremes) |
Application Data:
Recommended Thickness: Primer: 8 mils (200 ft²/gal), Finish Coat: 16 mils (100 ft²/gal)
Slurry (50% Silica Sand, 12 mils) : 125 ft²/gal
Trowel Epoxy (85% Silica Sand, 24 mils) : 60 ft²/gal
Fire Rating (CAN/ULC S102, ASTM E84) : Flame Spread: 5, Smoke Developed: 94 (Class A)
Property | Value |
Bond Resistance (ASTM D4541) | >300 psi (substrate ruptures) |
Hardness (Shore D, ASTM D2240) | 85–90 |
Abrasion Resistance (CS17 / 1000g / 1000 cycles) | 0.10 g loss |
Tensile Strength (ASTM D638) | 6500 psi |
Compressive Strength (ASTM D695) | 9000–10000 psi |
Elongation (ASTM D638) | 6–7% |
Substrate Temp | Foot Traffic | Light Traffic | Full Cure |
10°C (50°F) | N.A. | N.A. | N.A. |
20°C (68°F) | 1 day | 3 days | 7 days |
30°C (86°F) | 16 hrs | 2 days | 5 days |
Restrictions
- Application temp: 15°C–30°C (59°F–86°F)
- Max relative humidity: 85%
- Substrate moisture > 4% acceptable
- Avoid application on porous surfaces prone to humidity transfer
- Protect from moisture/condensation during first 24 hrs of cure
- May discolor under UV exposure