Two-component 100% solids epoxy coating system engineered to protect concrete and similar surfaces while offering rapid curing even in low temperatures. Delivers excellent mechanical and chemical resistance with a good aesthetic finish. Ideal for food and pharmaceutical environments due to its VOC-free, bacteria-resistant formulation.
- Rapid cure at ambient and low temperatures
- Excellent chemical and abrasion resistance
- VOC-free; low odor
- Excellent adhesion to substrates
- High resistance to water immersion and bacteria
- Stable under low-temperature water exposure
- Good working life
Item | Value |
Packaging | 11.35 L (3 US gal), 56.7 L (15 US gal) |
Color | Upon Request |
Recommended Thickness | 20 mils (80 ft²/gal) |
Shelf Life | 12 months (original sealed container, dry/cool) |
Mix Ratio by Volume | A:B = 2:1 (100:50) |
Mix Ratio by Weight | 100:47 |
Gel Time (100 g @ 25°C) | 25–30 minutes |
Solids by Weight/Volume | 100% / 100% |
VOC | 0 g/L (Zero VOC) |
Thinner Recommended | Xylene |
Component | Viscosity (cP) |
Part A | 1500–2500 |
Part B | 300 |
Mix | 1300–1500 |
Property | Value |
Specific Gravity | A: 1.14, B: 1.10, Mix: 1.13 |
Bond Strength (ASTM C882) | 400 psi (100% concrete failure) |
Shore D Hardness (ASTM D2240) | 85 |
Abrasion Resistance (ASTM D968) | 40 L sand / 1 dry mil |
Tensile Strength (ASTM C579) | 9000–10000 psi |
Compressive Strength (ASTM C579) | 8000–9000 psi |
Elongation (ASTM D638) | 4% |
Water Absorption (ASTM D570) | 0.3% |
Fire Rating (CAN/ULC S102, ASTM E84) | Flame Spread: 5, Smoke: 94 (Class A) |
Temp | Foot Traffic | Light Traffic | Full Cure |
10°C (50°F) | 6 hrs | 1 day | 7 days |
20°C (68°F) | 3 hrs | 1 day | 7 days |
30°C (86°F) | 12 hrs | 36 hrs | 5 days |
RESTRICTIONS
- Application temperature: 15°C–30°C (59°F–86°F)
- Max RH: 85%
- Substrate temperature ≥15°C and <4% moisture content
- Avoid porous ground-level exterior surfaces
- Protect for 24 hrs from humidity, water, condensation
- May discolor under UV light
Reagent | 3 Days | 7 Days | 28 Days |
Deionized Water | 0.30% | 0.51% | 1.11% |
Methanol | 6.38% | 8.94% | 9.55% |
Ethanol | 1.55% | 2.40% | 4.68% |
Xylene | 0.25% | 0.42% | 0.69% |
Lactic Acid | 1.10% | 1.64% | 3.24% |
Acetic Acid (10%) | 1.23% | 1.94% | 3.85% |
Sulfuric Acid (70%) | 0.10% | 0.10% | 0.13% |
Sodium Hydroxide (50%) | 0.04% | 0.05% | 0.09% |
Bleach | 0.27% | 0.45% | 0.93% |
1,1,1 Trichloroethane | 0.18% | 0.26% | 0.43% |
Nitric Acid (10%) | 0.55% | 0.92% | 2.05% |
Nitric Acid (30%) | 2.04% | 2.74% | 4.17% |
MEK | 9.36% | 13.48% | 11.10% |