High-build, solvent-free, two-component epoxy coating system designed for aggressive chemical environments. Offers exceptional resistance to chemicals and solvents. Ideal for use in manufacturing plants, labs, chemical facilities, food processing areas, and pharmaceutical environments. Compliant with C.F.I.A. regulations.
- Dense, non-porous surface resistant to bacteria and moisture
- VOC-compliant and odorless, suitable for interior use
- Can be recoated with excellent adhesion
- Exceptional chemical, solvent, and abrasion resistance
- Bonds well to many substrates
Item | Value |
Packaging | 11.35 L (3 US gal), 56.7 L (15 US gal) |
Color | Upon Request |
Recommended Thickness | 20 mils (80 ft²/gal) |
Shelf Life | 12 months (sealed, away from heat/moisture/light) |
Mix Ratio by Volume | A:B = 2:1 (100:50) |
Mix Ratio by Weight | A:B = 100:44 |
Gel Time (100 g @ 25°C) | 25–35 minutes |
VOC | Not stated (solvent-free) |
Thinner Recommended | Xylene |
Component | Viscosity (cP) |
Part A | 3500–4000 |
Part B | 300–350 |
Mix | 1300–1600 |
Property | Value |
Specific Gravity | Part A: 1.14–1.16, Part B: 1.02, Mix: 1.24–1.26 |
Bond Strength (ASTM C882) | 400 psi (100% concrete failure) |
Shore D Hardness (ASTM D2240) | 85 |
Abrasion Resistance (ASTM D4060) | 40 mg loss |
Tensile Strength (ASTM D638) | 9000–10000 psi |
Compressive Strength (ASTM D695) | 11000–12000 psi |
Elongation (ASTM D638) | 3–4% |
Water Absorption (ASTM D570) | 0.3% |
Fire Rating (CAN/ULC S102) | Flame Spread: 5, Smoke Developed: 94 |
Temp | Foot Traffic | Light Traffic | Full Cure |
10°C (50°F) | N/A | 1 day | 7 days |
20°C (68°F) | 1 day | 3 days | 7 days |
30°C (86°F) | 16 hrs | 2 days | 5 days |
RESTRICTIONS
- Application temp: 15°C–30°C (59°F–86°F)
- Max RH: 85%
- Substrate temperature must be ≥15°C and <4% moisture
- Avoid application on porous or ground-level exterior surfaces
- Protect from water, humidity, and condensation for first 24 hrs
- May discolor under UV exposure
Reagent | 3 Days | 7 Days | 28 Days |
Deionized Water | 0.46% | 0.75% | 1.32% |
Methanol | Destroyed | Destroyed | Destroyed |
Ethanol | 8.76% | 12.3% | Destroyed |
Xylene | 2.37% | 4.8% | 15.5% |
Lactic Acid | 0.63% | 1.01% | 1.70% |
Acetic Acid (10%) | 1.00% | 1.65% | 2.80% |
Sulfuric Acid (70%) | 0.11% | 0.10% | 0.11% |
Sodium Hydroxide (50%) | 0.05% | -0.03% | -0.04% |
Bleach | 0.41% | 0.65% | 1.05% |
Sulfuric Acid (98%) | Destroyed | Destroyed | Destroyed |
Toluene | 14.65% | 20.66% | Destroyed |
Skydrol | — | — | 1.83%, 3.10%, 5.60% |